TM52 Titanium Carbide Rod is a composite wear-resistant alloy material with titanium carbide as hard phase and high manganese steel as bonding phase. It has a density of about 6.1g/cm³ and a bending strength of 1400 - 1700MPa. It has work hardening phenomenon and can be cast or arc welded. It is non-magnetic and cannot be machined. It is mainly used for wear-resistant parts of crushing machinery and non-magnetic molds in mining and cement industries.
ADVANTAGES
Advantages:
1. Good weldability and castability. The steel bonded alloy matrix is a type of high manganese steel, which exists as a single austenite phase at room temperature and has high strength, which is beneficial for improving the resistance to thermal stress during casting. It can be welded with ordinary high manganese steel electrodes or connected to the substrate through casting, which is simple to operate and easy to produce, and can reduce manufacturing costs and shorten production cycles.
2. High hardness and wear resistance. A large amount of refractory metal carbides (titanium carbide) are dispersed in steel bonded alloys, which have high hardness; At the same time, the matrix is high manganese steel with work hardening characteristics, which greatly improves the wear resistance of the product.
3. Excellent cost-effectiveness. Compared with tungsten cobalt hard alloy, steel bonded alloy has a low density (about 6.0g/cm3, which is 40% of tungsten cobalt hard alloy) and has a good cost-effectiveness advantage.
Titanium Carbide Rod has their own unique comprehensive performance advantages due to their unique performance characteristics. This excellent comprehensive performance has broad application prospects in industries such as impact and crushing tools, mining, cement, and construction.
USE
Application:
When TM52 Titanium Carbide Rod is used in the wear-resistant parts of crushers, molten high manganese steel is used for casting, and the alloy rods are cast on the working surface of the wear-resistant parts. The two are firmly metallurgically bonded to form composite wear-resistant parts, which can solve the wear problems of high manganese steel and alloy steel wear-resistant parts of various crushers. It is widely used in various impact working conditions such as mining, cement sand making, etc.
SPECIFICATIONS
Specifications:
Common specifications are mainly round bars, including D12×40mm, D12×60mm, D14×50mm, D14×60mm, D14×70mm, D16×50mm, etc., which can also be customized.
| Grade | Binder Phase | Density | Hardness | TRS | Impact Toughness | |
| g/cm3 | Annealing | Hardening | Mpa | J/cm2 | ||
| HRC | HRA | |||||
| TM52 | Alloy Steel | 6.10-6.30 | Sintered state: HRC≥60 | ≥ 1500 | H2O toughing treatment ≥ 6.0 | |
1. φ12*40
2. φ12*60
3. φ14*50
4. φ14*70
5. φ14*80
6. φ14*90
7. φ16*50
8. φ16*60
9. φ16*70
10. φ20*40
11. φ20*60 （Spray-granulated Tic Rod）
12. φ20*80 （Spray-granulated Tic Rod）
PACKAGE
We support customized packaging ways.
RELATED PRODUCTS
Yuanxian High-tech Material is a company serving a worldwide customers base providing innovative and reliable product solution that recognizes the value of customer care.
+86 180 2006 1362
Haitai Huake Third Road No.1, Huayuan Industrial Zone, Binhai High Tech Zone, Tianjin, china
Quick Links
Product Category
Request a Quote
Welcome to subscribe toour email message!
Send a Message